انجمن علمی رنگ ایران مواد پیشرفته و پوشش های نوین 2322-1356 3 11 2014 06 21 Preparation, Electrochemical Properties and Stability of Sol-Gel Deriveed Nano-Composite Coating of Ni+Ru02 تهیه، خواص الکتروشیمیایی و پایداری پوشش های نانو کامپوزیت اکسید روتنیم به روش سل-ژل 777 786 69067 /2015.3.11.6 FA فریدون محمدی پژوهشگاه پلیمر و پتروشیمی، تهران Journal Article 2014 01 31 Nano-composite coating of Ni+Ru02 was prepared in acidic media by sol-gel technique and then heat treated at 350-400 oC. Electrochemical activity, surface properties and stability of the coating was investigated, considering the effect of alcohol adiition, by linear sweep voltametry (LSV), cyclic voltametry (CV) and chronopotentiometry, respectively. According to the LSV results, addition of Isobutyl alcohol to the sol solution having Ni+Ru02 resulted in a significant increase in exchange current density up to 0.61 MA/cm2 and a large decline in Tafel slope down to 39 mV/ decade. The cj'clic voltamograms obtained showed that the activity of the cathode coating did not decrease with time. The study of electrochemical stability of the coating by chronopotentiometry revealed that the sol-gel derived coating proved to be a suitable electrocatayst for hydrogen evolution reaction in alkaline media.   پوشش های نانوکامپوزیت اکسید روتنیم و نیکل به روش سل-ژل در محیط اسیدی جا تهیه و درC°۳۵۰ - ۴۰۰ حرارت دهی گردید. فعالیت الکتروشیمیایی، خواص سطحی و پایداری این پوشش ها با در نظر گرفت اثر افزایش الکل، به ترتیب با روش های ولتامتری روبش خطی (LSV), ولتامتری چرخه ای (CV) و کرنوپتانسیومتری بررسی<br />و مقایسه گردید. بر اساس نتایج LSV با افزودن الکل ایزوبوتیل به محلول سل حاوی روتنیم و نیکل، افزایش در شدت جریان تبادلی تا mA/ cm2 ۶۱/ و کاهش چشمگیر شیب تافل تاmVdecade ۳۹ حاصل گردید. نتایج ولتامتری چرخه ای نشان داد فعالیت پوشش های کاتدی تهیه شده با گذشت زمان کاهش نمی یابد. نتایج کرنوپتانسیومتری نیز بر پایداری الکتروشیمیایی این پوشش به عنوان الکتروکاتالیست مناسب جهت تولید هیدروژن در محیط های قلیایی تاکید ورزید.